Commercial water dispersions of Fe/Fe–O nanoparticles (!50–80nm diameter) were prepared bare and treated with a biodegradable polymer to stabilize the suspension. Hysteresis loops and FC–ZFC curves of samples in liquid and dried form were measured by means of a vibrating sample magnetometer from 77 to 300 K. A marked dependence on the conditioning field is observed in all samples that display the Verwey transition at about 120 K. The role of magnetic interactions on dried samples was also investigated by means of magnetoresistance measurements as a function of temperature

Temperature dependence of magnetic properties in in Fe/Fe-O nanoparticles dispersed in water / Coisson, Marco; Celegato, F.; DALLA VECCHIA, ELENA CRISTINA; Sethi, Rajandrea; Tiberto, P.; Vinai, F.. - In: JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS. - ISSN 0304-8853. - ELETTRONICO. - 321:14(2009), pp. 2276-2278. [10.1016/j.jmmm.2009.01.039]

Temperature dependence of magnetic properties in in Fe/Fe-O nanoparticles dispersed in water

COISSON, Marco;DALLA VECCHIA, ELENA CRISTINA;SETHI, RAJANDREA;
2009

Abstract

Commercial water dispersions of Fe/Fe–O nanoparticles (!50–80nm diameter) were prepared bare and treated with a biodegradable polymer to stabilize the suspension. Hysteresis loops and FC–ZFC curves of samples in liquid and dried form were measured by means of a vibrating sample magnetometer from 77 to 300 K. A marked dependence on the conditioning field is observed in all samples that display the Verwey transition at about 120 K. The role of magnetic interactions on dried samples was also investigated by means of magnetoresistance measurements as a function of temperature
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11583/1920485
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo