In this paper the influence of DCT (Deep Cryogenic Treatment) and a CrN arc-deposited PVD (Physical Vapor Deposition) coating on the fatigue behaviour of AISI 302 stainless steel was studied. Rotating bending tests were carried out on standard specimens to evaluate the fatigue limit at 300000 load cycles. The single and the combined effects of the two treatments were investigated by addressing untreated, PVD-coated and both PVD-coated and DC-treated specimens to the tests. All the series of specimens were also tested statically and laboratory analyses including fracture surface SEM observations and hardness measurements were performed.

Study of the Effect of DCT and PVD Treatments on the Fatigue Behaviour of AISI 302 Stainless Steel / Baldissera, Paolo; Cavalleri, S; Marcassolii, P; Tordini, F. (KEY ENGINEERING MATERIALS). - In: Advances in Fracture and Damage Mechanics VIII / Aliabadi MH, Abela S, Baragetti S, Guagliano M, Lee H-S. - STAMPA. - Uetikon : Trans Tech Publications, 2010. - ISBN 978-0-87849-315-9. - pp. 49-52 [10.4028/www.scientific.net/KEM.417-418.49]

Study of the Effect of DCT and PVD Treatments on the Fatigue Behaviour of AISI 302 Stainless Steel

BALDISSERA, PAOLO;
2010

Abstract

In this paper the influence of DCT (Deep Cryogenic Treatment) and a CrN arc-deposited PVD (Physical Vapor Deposition) coating on the fatigue behaviour of AISI 302 stainless steel was studied. Rotating bending tests were carried out on standard specimens to evaluate the fatigue limit at 300000 load cycles. The single and the combined effects of the two treatments were investigated by addressing untreated, PVD-coated and both PVD-coated and DC-treated specimens to the tests. All the series of specimens were also tested statically and laboratory analyses including fracture surface SEM observations and hardness measurements were performed.
2010
978-0-87849-315-9
Advances in Fracture and Damage Mechanics VIII
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11583/2263512
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo