In the recent years the interest of the research community towards multiferroic composite materials was growing fast [1,2]. A number of papers relates to bulk materials while less attention is focused on films. Electrophoretic deposition (EPD) was applied to prepare magnetoelectric (ME) composite bilayer thick films based on perovskite phase and spinel cobalt ferrite as some of the best piezoelectric and magnetostrictive oxides belong these crystal groups. The co-deposition of titanium oxide (TO) and cobalt ferrite (CFO) nanoparticles and the deposition of niobium-doped lead titanate zirconate (PZTN) were made from colloidal suspensions in ethanol keeping constant voltage and recording the current. Good adhesion and compaction of the green film were achieved by optimization of deposition voltage and time while high density of the film and minimized interphase reactions occurred after sintering. The deposited volume, the mixing of dielectric and magnetic phases and the density and ordering of the films have been verified by electron scanning microscopy after heat treatment. No reactions between the different phases was found. The piezoelectric properties were measured on the sintered films. [1] N.A. Spaldin, M. Fiebig, Science 309 (2005) 391. [2] R. Ramesh, N.A. Spaldin, Nat. Mater. 6 (2007) 21.
Magnetoelectric composite bilayer film by electrophoretic deposition / Galizia, Pietro; Gardini, Davide; Galassi, Carmen. - ELETTRONICO. - (2015). (Intervento presentato al convegno 4th Conference of the Italian Magnetism Association (AIMagn) - MAGNET 2015 tenutosi a Bologna (Italy) nel February 17-19, 2015).
Magnetoelectric composite bilayer film by electrophoretic deposition
GALIZIA, PIETRO;
2015
Abstract
In the recent years the interest of the research community towards multiferroic composite materials was growing fast [1,2]. A number of papers relates to bulk materials while less attention is focused on films. Electrophoretic deposition (EPD) was applied to prepare magnetoelectric (ME) composite bilayer thick films based on perovskite phase and spinel cobalt ferrite as some of the best piezoelectric and magnetostrictive oxides belong these crystal groups. The co-deposition of titanium oxide (TO) and cobalt ferrite (CFO) nanoparticles and the deposition of niobium-doped lead titanate zirconate (PZTN) were made from colloidal suspensions in ethanol keeping constant voltage and recording the current. Good adhesion and compaction of the green film were achieved by optimization of deposition voltage and time while high density of the film and minimized interphase reactions occurred after sintering. The deposited volume, the mixing of dielectric and magnetic phases and the density and ordering of the films have been verified by electron scanning microscopy after heat treatment. No reactions between the different phases was found. The piezoelectric properties were measured on the sintered films. [1] N.A. Spaldin, M. Fiebig, Science 309 (2005) 391. [2] R. Ramesh, N.A. Spaldin, Nat. Mater. 6 (2007) 21.File | Dimensione | Formato | |
---|---|---|---|
2015-02-MAGNET2015-Poster.pdf
accesso aperto
Descrizione: Poster Presented at the MAGNET2015 Conference
Tipologia:
Altro materiale allegato
Licenza:
PUBBLICO - Tutti i diritti riservati
Dimensione
1.52 MB
Formato
Adobe PDF
|
1.52 MB | Adobe PDF | Visualizza/Apri |
Pubblicazioni consigliate
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.
https://hdl.handle.net/11583/2646547
Attenzione
Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo