Co-deposition of CuO and Mn1.5Co1.5O4by single step electrophoretic deposition is used to produce15mm coatings on Crofer22APU steel, which finds use as interconnect for high temperature solid oxide cells.Sintering of the green coatings in reducing and then oxidizing conditions led to formation of a mixed (Cu,Mn,Co)3O4spinel. By the incorporation of Cu, the density of the coatings improved. Scanning and trans-mission electron microscopy observations, supplemented with energy dispersive spectroscopy, con-firmed dissolution of Cu in the spinel phase. For the un-doped Mn1.5Co1.5O4both the tetragonal andcubic phases are detected at room temperature by X-ray diffractometry, whereas the addition of Cuseems to stabilize the cubic phase. Initial (1000 h) high temperature corrosion evaluation at 800°Cin air showed promising properties of the mixed spinel coating.

Co-deposition of CuO and Mn1.5Co1.5O4 powders on Crofer22APU by electrophoretic method: Structural, compositional modifications and corrosion properties / Sebastian, Molin; Sabato, ANTONIO GIANFRANCO; Javed, Hassan; Grzegorz, Cempura; Aldo Roberto Boccaccini, ; Smeacetto, Federico. - In: MATERIALS LETTERS. - ISSN 0167-577X. - 218:(2018), pp. 329-333. [10.1016/j.matlet.2018.02.037]

Co-deposition of CuO and Mn1.5Co1.5O4 powders on Crofer22APU by electrophoretic method: Structural, compositional modifications and corrosion properties

Antonio Gianfranco Sabato;JAVED, HASSAN;Federico Smeacetto
2018

Abstract

Co-deposition of CuO and Mn1.5Co1.5O4by single step electrophoretic deposition is used to produce15mm coatings on Crofer22APU steel, which finds use as interconnect for high temperature solid oxide cells.Sintering of the green coatings in reducing and then oxidizing conditions led to formation of a mixed (Cu,Mn,Co)3O4spinel. By the incorporation of Cu, the density of the coatings improved. Scanning and trans-mission electron microscopy observations, supplemented with energy dispersive spectroscopy, con-firmed dissolution of Cu in the spinel phase. For the un-doped Mn1.5Co1.5O4both the tetragonal andcubic phases are detected at room temperature by X-ray diffractometry, whereas the addition of Cuseems to stabilize the cubic phase. Initial (1000 h) high temperature corrosion evaluation at 800°Cin air showed promising properties of the mixed spinel coating.
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11583/2701015
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo