In heavy loaded mating components, such as sliders and sliding bearings, guaranteeing the efficiency of lubricant films for long times during severe service conditions is very complicated. In this work, the benefits deriving from the use of fiber laser sources for surface texturing of very thin TiN coatings in severe wear working conditions were demonstrated. Evaluations of the laser textured dimples shape, geometry and density are given. Wear performance of the fiber laser textured surfaces was evaluated in discontinuous oil lubricated conditions with a flat contact. High normal load and low sliding speed were applied. Comparison tests were also performed on commercial TiN and WC/C coatings. In terms of average wear volume and maximum wear depth, Laser Surface Texturing of TiN provided respectively a 70% and a 45% reduction if compared to plain TiN. If compared to WC/C the wear resistance gains were lower but LST TiN maintained such benefits for longer wear runs. SEM analysis also revealed that the laser interaction provided a localized thermal cracking to the TiN coating. However, the sliding action caused very limited and localized coating fragmentation or delamination.

Wear Behavior of Fiber Laser Textured TiN Coatings in a Heavy Loaded Sliding Regime / Vandoni, Laura; Demir, A. G.; Previtali, B.; Lecis, N.; Ugues, Daniele. - In: MATERIALS. - ISSN 1996-1944. - ELETTRONICO. - 5:(2012), pp. 2360-2382. [10.3390/ma5112360]

Wear Behavior of Fiber Laser Textured TiN Coatings in a Heavy Loaded Sliding Regime

VANDONI, LAURA;UGUES, Daniele
2012

Abstract

In heavy loaded mating components, such as sliders and sliding bearings, guaranteeing the efficiency of lubricant films for long times during severe service conditions is very complicated. In this work, the benefits deriving from the use of fiber laser sources for surface texturing of very thin TiN coatings in severe wear working conditions were demonstrated. Evaluations of the laser textured dimples shape, geometry and density are given. Wear performance of the fiber laser textured surfaces was evaluated in discontinuous oil lubricated conditions with a flat contact. High normal load and low sliding speed were applied. Comparison tests were also performed on commercial TiN and WC/C coatings. In terms of average wear volume and maximum wear depth, Laser Surface Texturing of TiN provided respectively a 70% and a 45% reduction if compared to plain TiN. If compared to WC/C the wear resistance gains were lower but LST TiN maintained such benefits for longer wear runs. SEM analysis also revealed that the laser interaction provided a localized thermal cracking to the TiN coating. However, the sliding action caused very limited and localized coating fragmentation or delamination.
2012
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11583/2504465
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo