Archivio Istituzionale della RicercaThe interplay between chemical composition, plastic behavior, and fracture modes of Cu46.5Zr46.5Al7 and Cu46.5Zr41.5Al7Y5 bulk metallic glasses (BMGs) was investigated by compression tests and fracture surfaces analyses. The aim was to explore the possibility of coupling physical, chemical, and hardness properties, with adequate macroscopic compressive plasticity. Cylindrical test samples, having a height-to-diameter ratio equal to 2, were machined and ground from as-cast bars and were tested in compression between lubricated plates, the displacement being measured by a clip-gage inserted between the plates. Y free BMG engineering stress-strain curves show a plastic behavior consisting of successive sudden stress drops and linear reloading segments. A detailed analysis of these features was performed to yield a correlation between the plastic deformation steps and the released elastic energy associated with each serration.
Fracture behavior in Cu46.5Zr46.5Al7 and Cu46.5Zr41.5Al7Y5 bulk metallic glasses / Matteis, Paolo; RUSSO SPENA, Pasquale; Pozzi, Chiara; Baser, T. A.; Baricco, M.; Battezzati, L.; Firrao, Donato; Castellero, A.. - In: METALLURGICAL AND MATERIALS TRANSACTIONS. A, PHYSICAL METALLURGY AND MATERIALS SCIENCE. - ISSN 1073-5623. - STAMPA. - 41:(2010), pp. 1767-1774. [10.1007/s11661-010-0266-7]
Fracture behavior in Cu46.5Zr46.5Al7 and Cu46.5Zr41.5Al7Y5 bulk metallic glasses.
MATTEIS, PAOLO;RUSSO SPENA, PASQUALE;POZZI, CHIARA;FIRRAO, Donato;
2010
Abstract
The interplay between chemical composition, plastic behavior, and fracture modes of Cu46.5Zr46.5Al7 and Cu46.5Zr41.5Al7Y5 bulk metallic glasses (BMGs) was investigated by compression tests and fracture surfaces analyses. The aim was to explore the possibility of coupling physical, chemical, and hardness properties, with adequate macroscopic compressive plasticity. Cylindrical test samples, having a height-to-diameter ratio equal to 2, were machined and ground from as-cast bars and were tested in compression between lubricated plates, the displacement being measured by a clip-gage inserted between the plates. Y free BMG engineering stress-strain curves show a plastic behavior consisting of successive sudden stress drops and linear reloading segments. A detailed analysis of these features was performed to yield a correlation between the plastic deformation steps and the released elastic energy associated with each serration.
| File | Dimensione | Formato | |
|---|---|---|---|
|
2372103.pdf
accesso aperto
Tipologia:
2. Post-print / Author's Accepted Manuscript
Licenza:
PUBBLICO - Tutti i diritti riservati
Dimensione
631.69 kB
Formato
Adobe PDF
|
631.69 kB | Adobe PDF | Visualizza/Apri |
Pubblicazioni consigliate
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.
https://hdl.handle.net/11583/2372103
Attenzione
Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo